ER308L MIG Welding Wire #2
Description
AWS A5.9 ER308L
Diameter: ?0.8mm-?2.0mm
Package: 1Kg/Spool, 5Kg/Spool, 15Kg/Spool, 20Kg/Spool, 100Kg/Drum, 2000Kg/Drum, 250Kg/Drum
Description:
ER308L is similar to ER308 but contains an average 0.02% carbon producing a weld deposit with good resistance against intergranular corrosion caused by carbide precipitation. ER308L is commonly used for welding AISI types 304L, 308L, 321 and 347.
Chemical Composition of Deposited Metal(%):
| Test item | C | Si | Mn | P | S | Cr | Ni | Mo | Cu |
| Standard | ??.030 | 0.30-0.65 | 1.00-2.50 | ??.030 | ??.030 | 19.5-22.00 | 9.00-11.00 | ??.75 | ??.75 |
| Actural Result | 0.020 | 0.43 | 1.55 | 0.011 | 0.008 | 20.35 | 10.05 | 0.34 | 0.15 |
Mechanical Properties of Deposited Metal:
| Tensile strengthRm(MPa) | Elongation(%) | |
| Standard | ??80 | ??5 |
| Actural Result | 510 | 32 |
Notes:
- MIG welding: Power supply polarity DC+.
- Shielding gas flow rate should be 15~25L/min.
- Shielding gas: Must ensure not to operate with impurity shield gas. Recommended ratio of mixed gas: Ar+1-3% O2.
- During welding, oil, rust, moisture, and other impurities at the weld joint should be strictly removed.
- The selection of welding wire should be based on the composition of the base metal being welded, using the same alloy system; the welding wire composition should be as close as possible to (equal to or slightly higher than) the base metal composition.